Yinong WANG
,
J.C.Huang
材料科学技术（英）
A two-stage strain rate deformation method is proposed to enhance the superplasticity in a hot extruded AZ61 alloy. In the stage-one of deformation, a relatively high strain rate was applied in order to obtain fine grains through dynamic recrystallization. The optimum strain rate for DRX at 300℃ was identified as ～5×10-3 s-1. Stage-two is conducted at relatively low strain rate in order to utilize the fine grains refined by DRX during stage-one to make the grain boundary sliding operate more smoothly, which resulting in enhanced superplastic elongation from 350% to 440%.
关键词:
AZ61 magnesium alloy
,